Saves: OLD ZINC DIE CAST SCRAP
Shall consist of miscellaneous old zinc base die castings, with or without iron and other foreign attachments. Must be free of borings, turnings, dross pieces, chunks, melted pieces and skimmings. All unmeltables, dirt, foreign attachments, and volatile substances (such as rubber, cork, plastic, grease, etc.) are deductible. Material containing in excess of 30% iron will not constitute good delivery.
Scabs: NEW ZINC DIE CAST SCRAP
Shall consist of new or unused, clean, zinc base die castings. Castings to be unplated, unpainted, and free from corrosion.
Scoot: ZINC DIE CAST AUTOMOTIVE GRILLES
Shall consist of clean, old or used zinc base die cast automotive grilles, free from soldered material. All foreign
attachments and extraneous materials are deductible.
Scope: NEW PLATED ZINC DIE CAST SCRAP
Shall consist of new or unused clean, plated zinc base die castings, free from corrosion.
Score: OLD SCRAP ZINC
Shall consist of clean dry scrap zinc, such as sheets, jar lids, clean unalloyed castings and anti-corrosion plates. Borings and turnings are not acceptable. Material must not be excessively corroded or oxidized. All foreign attachments and extraneous materials are deductible.
Screen: NEW ZINC CLIPPINGS
Shall consist of any new pure zinc sheets or stampings free from corrosion. To contain no foreign material or attachments. Printers zinc, such as engravers zinc, lithograph sheets and addressograph plates subject to special arrangements. Printers zinc to be free of routings.
Scribe: CRUSHED CLEAN SORTED FRAGMENTIZERS DIE CAST SCRAP, AS PRODUCED FROM AUTOMOBILE FRAGMENTIZERS
To be clean, free of dirt, oil, glass, rubber, and trash. To contain a maximum of 5% unmeltables such as free iron, copper, aluminum and other metals.
Scroll: UNSORTED ZINC DIE CAST SCRAP
Produced from automobile fragmentizers. Material to contain about 55%zinc-bearing scrap. Other non-ferrous metals such as aluminum, stainless steel, redmetal, etc, to be about 40%. Insulated copper wire about 1%. Trash, dirt, glass, rubber, oil, iron, not to exceed 5%. Any variations to be sold by special arrangement between buyer and seller.
Scrub: HOT DIP GALVANIZERS SLAB ZINC DROSS (Batch Process)
Shall consist only of galvanizers unsweated zinc dross in slab form from hot dip galvanizing (Batch Process) with a minimum zinc content of 92%and shall be free of skimmings and tramp iron. Broken pieces under 2"
in diameter shall not exceed 10%of the weight of each shipment. Slabs shall not weigh over 100 pounds each.
Heavier pieces acceptable upon mutual agreement between buyer and seller. Material from continuous galvanizing operation is not acceptable. Blocks are acceptable upon mutual agreement.
Scull: ZINC DIE CAST SLABS OR PIGS
Shall consist of melted zinc base die cast materials, in smooth clean solid slabs or pigs. Material to be free
From drosses and to contain a minimum zinc content of 90%. To contain a maximum of 0.1%nickel and
Maximum of 1%lead. Blocks are acceptable upon mutual agreement.
Seal: CONTINUOUS LINE GALVANIZING SLAB ZINC TOP DROSS
Shall consist of unsweated zinc dross removed from the top of a continuous line galvanizing bath, in slab form not weighing in excess of 100 pounds each, with a minimum zinc content of 90%. Heavier pieces acceptable upon mutual agreement between buyer and seller. Shall be free of skimmings. Broken pieces under 2" in diameter shall not exceed 10%of the weight of each shipment.
Seam: CONTINUOUS LINE GALVANIZING SLAB ZINC BOTTOM DROSS
Shall consist of unsweated zinc dross removed from the bottom of a continuous line galvanizing bath, in slab form not weighing in excess of 100 pounds each, with a minimum zinc content of 92%. Heavier pieces acceptable upon mutual agreement between buyer and seller. Shall be free of skimmings. Broken pieces under 2" in diameter shall not exceed 10%of the weight of each shipment.
Shelf: PRIME ZINC DIE CAST DROSS
Shall consist of metal skimmed from the top of pot of molten zinc die cast metal. Must be unsweated, unfluxed, shiny, smooth, metallic and free from corrosion or oxidation. Should be poured in molds or in small mounds weighing not over 75 pounds each. Zinc content shall be minimum of 85%.
Wafer: MAGNESIUM CLIPS
Shall consist of clean magnesium clips in crucible size, free of copper, aluminum, and zinc flashings and excessive oil and grease. To be free of all foreign attachments.
Walnut: MAGNESIUM SCRAP
Shall consist of magnesium castings, magnesium engine blocks and transmission casings, bomber and car wheels, extrusions, and sheet. Material to be free from brass and copper inserts and all foreign attachments. To be free of anodes, hollow castings and explosives. Percentages of and penalties for dirt, oil, grease, and iron to be subject to agreement between buyer and seller. Excessively large pieces to be negotiated between buyer and seller.
Wine: MAGNESIUM ENGRAVER PLATES
To be free of copper, aluminum, zinc, and electrotype plates. To be clean and free of all foreign attachments. Magnesium plates shipped loose by agreement between buyer and seller.
Wood: MAGNESIUM DOCKBOARDS
Shall consist of clean magnesium dock board cut or broken to size agreed upon by buyer and seller. To be
free of all foreign attachments.
World: MAGNESIUM TURNINGS
It is recommended that these materials be sold by special arrangement between buyer and seller. |